LORD 1110
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- Low-Density Epoxy Foam
- Extended Working Time
- High Compressive Strength
Product Description
LORD 1110 A/B Syntactic Foam is a modified epoxy syntactic foam system formulated for applications requiring low density, high compressive strength, and extended working time. The two-component material mixes at a 100:50 weight ratio and produces a non-sag white paste suitable for vertical application and gap-filling. It cures at room temperature or with accelerated heat cure, providing flexibility for manufacturing processes. Once cured, the foam can be shaped by sanding, drilling, or cutting, making it suitable for applications where lightweight structural support and machinability are important considerations.
Key features
- Low-density epoxy foam: Mixed density of 600–700 kg/m³ helps reduce overall assembly weight while maintaining structural performance.
- Extended working time: Provides approximately 60 minutes of working time at 25°C, supporting complex application and assembly processes.
- High compressive strength: Delivers compressive strengths up to 9000 psi (62.1 MPa) when heat cured, supporting demanding structural applications.
Applications / Suitable for
- Lightweight structural filling applications
- Vertical gap-filling and contour-forming operations
- Assemblies requiring machinable cured foam
- Applications where low density and high compressive strength are important evaluation criteria
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Additional Information
As-supplied / before-processing properties
Representative as-supplied properties and processing characteristics.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Mix Ratio | 100:50 | By weight | Part A : Part B |
| Mixed Density | 600–700 | kg/m³ | Mixed material |
| Working Time | 60 | min | 25°C |
| Appearance | White Paste | — | Mixed material |
After-processing / final-state properties
Representative cured properties. Values are typical and not specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Hardness | 60 | Shore D | Cured |
| Tensile Shear Strength | 3100 | psi | 25°C |
| Compressive Strength | 8000 | psi | 1 hour cure @ 121°C |
| TML Outgassing | 0.99 | % | ASTM E595 |